In this study, Fire Retardant (FR) chemicals with different proportions were added into fibers and high density fiberboards (HDF) were produced using fibers from Scots pine and beech (50:50). HDF panels containing 3%, 6%, and 9% borax, boric acid, ammonium polyphosphate and alpha-x chemicals powders were manufactured. Limiting oxygen index (LOI) and thermal conductivity properties of HDF panels were determined. FR chemicals improved the LOI and thermal conductivity. However, this improvement was affected by the type and the concentration of the FR chemicals used. The best thermal conductivity result was obtained with 9% boric acid concentrations (0.2815 W/moK) while the best LOI results were obtained from 6% and 9% ammonium polyphosphate concentrations (45%). Keywords: HDF, Borax, Boric acid, Thermal conductivity, LOI
Bu çalışmada, yanmayı geciktirici bazı kimyasal maddeler değişik oranlarda lif ile muamele edilmiş ve yüksek yoğunluklu liflevha (HDF) üretilmiştir. Hammadde olarak %50 kayın ve %50 sarıçam lifleri kullanılmıştır. Liflerin içine tam kuru lif miktarına oranla %3, %6, %9 oranlarında toz halinde boraks, borik asit, amonyum polifosfat ve alfa-x kimyasalları ilave edilerek HDF levhalar elde edilmiştir. Elde edilen yüksek yoğunluklu lif levhanın ısı iletkenliği ve limit oksijen indeksi (LOI) değerleri belirlenmiştir. Yanmayı geciktirici kimyasal maddelerin ısı iletkenliği ve limit oksijen miktarını artırdığı ancak kimyasal madde türü ve konsantrasyon oranına göre farklı etki yaptıkları tespit edilmiştir. Isı iletkenliği için en iyi sonuç %9' luk borik asit (0.2815 W/moK) ile sağlanırken LOI testi için en iyi sonuçlar %6 ve %9' luk amonyum polifosfat (%45) için elde edilmiştir.Anahtar Kelimeler: HDF, Boraks, Borik asit, Isı iletkenliği, LOI